6110A aluminum bar is mainly alloyed with magnesium and silicon, and is particularly suitable for forging and hollow extrusion products. It has the highest tensile strength among the 6000 series alloys, and exhibits excellent bendability and high processability.
This aluminum alloy is widely used in building structures, mechanical equipment, transportation and other fields, especially in scenes requiring high strength and lightness, showing excellent performance and diverse applicability.
Specification of MASTAR 6110A aluminum bar
Equivalent Names: UNS A96110; Aluminium 6110A; AA6110A; Al6110A
Temper: 6110A-T4, 6110A-T5, 6110A-T6
Product type: 6110 aluminum round bar, 6110 aluminum flat bar, 6110 aluminum square bar, 6110 aluminum forged bar, other custom shapes aluminum bar
Surface treatment: mill finish, Anodizing, brushed, mirror, embossing, etc.
Specification: EN 573-3: 2009, EN 755-2: 2008, ASTM B317/SAE J454
6110A aluminum chemical composition
| Element | Composition (%) |
| Aluminum (Al) | 94.8 to 98 |
| Silicon (Si) | 0.7 to 1.1 |
| Magnesium (Mg) | 0.7 to 1.1 |
| Manganese (Mn) | 0.3 to 0.9 |
| Copper (Cu) | 0.3 to 0.8 |
| Iron (Fe) | 0 to 0.5 |
| Chromium (Cr) | 0.050 to 0.25 |
| Titanium (Ti) | 0 to 0.2 |
| Zirconium (Zr) | 0 to 0.2 |
| Zinc (Zn) | 0 to 0.2 |
6110A aluminum bar mechanical property
| Temper | Tensile strength Ultimate (MPa) | Tensile Strength: Yield (Proof) (MPa) | A-Min. elongation at fracture (%) | A-Min. elongation Lo=50mm (%) | Brinell hardness (HBW) |
| 6110-T4 | 320 | 220 | 16 | 14 | 85 |
| 6110-T5 | 380 | 360 | 10 | 8 | 115 |
| 6110-T6 | 380-410 | 360-380 | 10 | 8 | 120 |
MASTAR 6110A aluminum rod product advantages
- High strength and hardness: 6110A aluminum bar exhibits excellent strength and hardness after heat treatment, making it excel in high stress and high load environments.
- Good corrosion resistance: 6110A aluminum alloy has good corrosion resistance and is particularly suitable for humid and corrosive environments.
- Excellent processing performance: 6110A aluminum bar has good cutting and welding performance, suitable for various complex mechanical processing and manufacturing processes.
- Excellent bendability: good bendability during molding and processing allows for complex shape design without affecting the overall strength and performance of the material.
- Lightweight material: compared to other high-strength materials, 6110A aluminum alloy is lightweight, helping to reduce the overall weight of the finished product, improving fuel efficiency and performance.
MASTAR 6110A aluminum bar cooperation areas
6110A aluminum bar is widely used in many fields due to its excellent performance characteristics. Whether it is building structure, mechanical equipment or transportation, 6110A aluminum bar has demonstrated its high strength, excellent processing performance and durability.
6110A aluminum bar in the automotive industry- Suitable for manufacturing body structures, chassis components and high-performance engine parts, helping to reduce vehicle weight and improve fuel efficiency.
6110A aluminum bar in aerospace applications- Due to its high strength and lightweight properties, 6110A aluminum bars are often used to manufacture aircraft structures, spacecraft components, and other high-performance aerospace products.
6110A aluminum bar in shipbuilding- 6110A aluminum bars are used to manufacture hull structures, deck components and other important parts, providing corrosion resistance and high strength.
6110A aluminum bar in mechanical equipment- It is widely used in the manufacture of various mechanical equipment and tools, such as high-precision molds, mechanical parts and structural parts.
Electronics and electrical engineering- Used to manufacture electronic components and electrical equipment that require high conductivity and corrosion resistance, improving product performance and life.